Filamont Standard Pro Resin 2.0 (Clear)
Filamont Standard Pro Resin 2.0 (Mango)
Filamont Standard Pro Resin 2.0 (Orange Red)
Filamont Photopolymer Model Resin (Nebula grey)
Filamont Photopolymer Model Resin (Brown)
Filamont 14K Pro Resin (Mango) ā Precision Perfected, Beyond 10K & 12K Limits
Filamont 14K Pro Resin (Orange Red) ā Precision Perfected, Beyond 10K & 12K Limits
Filamont Water Washable 3D Printer Resin (White)
- Density (g/cm³ @25ā): 1.05-1.25
- Viscosity (cps @25ā): 100-350
- Tensile Strength (MPa): 55.80
- Tensile Modulus (MPa): 2327.00
- Elongation at Break: 10.90%
- Flexural Strength (MPa): 73.85
- Flexural Modulus (MPa): 1924.00
- Impact Value (J/m): 77.18
- Heat Deflection Temperature (ā @0.45 MPa): 61.50
- Hardness: 80-85D
- Tear Strength (kN/m): N/A
Filamont Water Washable 3D Printer Resin (Skin)
- Density (g/cm³ @25ā): 1.05-1.25
- Viscosity (cps @25ā): 100-350
- Tensile Strength (MPa): 55.80
- Tensile Modulus (MPa): 2327.00
- Elongation at Break: 10.90%
- Flexural Strength (MPa): 73.85
- Flexural Modulus (MPa): 1924.00
- Impact Value (J/m): 77.18
- Heat Deflection Temperature (ā @0.45 MPa): 61.50
- Hardness: 80-85D
- Tear Strength (kN/m): N/A
Filamont Water Washable 3D Printer Resin (Orange Red)
- Density (g/cm³ @25ā): 1.05-1.25
- Viscosity (cps @25ā): 100-350
- Tensile Strength (MPa): 55.80
- Tensile Modulus (MPa): 2327.00
- Elongation at Break: 10.90%
- Flexural Strength (MPa): 73.85
- Flexural Modulus (MPa): 1924.00
- Impact Value (J/m): 77.18
- Heat Deflection Temperature (ā @0.45 MPa): 61.50
- Hardness: 80-85D
- Tear Strength (kN/m): N/A
Filamont Water Washable 3D Printer Resin (Grey)
- Density (g/cm³ @25ā): 1.05-1.25
- Viscosity (cps @25ā): 100-350
- Tensile Strength (MPa): 55.80
- Tensile Modulus (MPa): 2327.00
- Elongation at Break: 10.90%
- Flexural Strength (MPa): 73.85
- Flexural Modulus (MPa): 1924.00
- Impact Value (J/m): 77.18
- Heat Deflection Temperature (ā @0.45 MPa): 61.50
- Hardness: 80-85D
- Tear Strength (kN/m): N/A
Filamont Water Washable 3D Printer Resin (Black)
- Density (g/cm³ @25ā): 1.05-1.25
- Viscosity (cps @25ā): 100-350
- Tensile Strength (MPa): 55.80
- Tensile Modulus (MPa): 2327.00
- Elongation at Break: 10.90%
- Flexural Strength (MPa): 73.85
- Flexural Modulus (MPa): 1924.00
- Impact Value (J/m): 77.18
- Heat Deflection Temperature (ā @0.45 MPa): 61.50
- Hardness: 80-85D
- Tear Strength (kN/m): N/A